Unless otherwise noted crystal structure is '''simple cubic like table salt NaCl'''. <br> | Unless otherwise noted crystal structure is '''simple cubic like table salt NaCl'''. <br> | ||
| − | Typical (with a few exceptions) is '''1900°C | + | Typical (with a few exceptions) is '''1900°C melting point and Mohs 5'''. |
* ScO - no monoxide? (well its a rare earth anyway) | * ScO - no monoxide? (well its a rare earth anyway) | ||
| Line 20: | Line 20: | ||
* [[Binary gem-like compound]] | * [[Binary gem-like compound]] | ||
| + | |||
| + | == External links == | ||
| + | |||
| + | * [https://en.wikipedia.org/wiki/Category:Transition_metal_oxides Wikipedia Category:Transition_metal_oxides] | ||
Revision as of 22:30, 12 April 2021
Unless otherwise noted crystal structure is simple cubic like table salt NaCl.
Typical (with a few exceptions) is 1900°C melting point and Mohs 5.
- ScO - no monoxide? (well its a rare earth anyway)
- TiO - Titanium(II)_oxide - mineral: hongquiit - 4.96g/ccm - Mohs ?? - 1,750°C
- VO - Vanadium(II)_oxide - no mineral - 5.758g/ccm - Mohs ?? - 1,789 °C
- CrO - Chromium(II)_oxide - no mineral - only powders by thermodynamic means - 300°C (low!)
- MnO - Manganese(II)_oxide - Manganosite - 5.364g/ccm - Mohs 5 to 6 - 1,945 °C - water insoluble
- FeO - Iron(II)_oxide - Wüstite - 5.7g/ccm - Mohs 5.0 to 5.5 - 1,377°C - water insoluble
- CoO - Cobalt(II)_oxide - no mineral? - 6.45g/ccm - Mohs ?? - 1,933°C - water insoluble
- NiO - Nickel(II)_oxide - Bunsenite 6.898g/ccm - Mohs 5.5 - 1,955°C - watersolubility negligible
- CuO - Copper(II)_oxide - tenorite 6.5g/ccm - Mohs 3.5 to 4.0 - Monoclinic - 1,326 °C - water insoluble
- ZnO - Zinc_oxide - [1] - 5.64–5.68g/ccm - Mohs 4 - Hexagonal - 1,974°C (decomposes) - watersolubility minute